Unshaped refractories include products such as mortars, plastics, ramming and gunning mixes and castables. Supplied in bulk or packaged unshaped, so that they can be used directly in place, resulting in, many times, large monolithic structures. They may be applied by hot or cold gunning to make new structures or for repair work of linings which are already in operation.
Our castables may be adjusted to special application conditions such as: pumping, shotcrete, free flow, gunning, set time, temperature of application.
Please consult our Technical Department for information on the best possible material for your equipment. |
|
|
|
| |
| Recomendadas para projeção pneumática a quente ou a frio, necessárias para os reparos das alvenarias dos equipamentos metalúrgicos básicos. Fornecidas em sacos multifolhados de papel ou em big bag. |
Recommended for hot and cold gunning, necessary for brick repair work in basic metallurgical equipment. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
| |
M |
Fe2O3 |
| JETOG-FE |
82,4 |
2,1 |
| JETOG-2873 |
80,0 |
1,6 |
| JETOG-3804 |
78,1 |
2,1 |
| Recomendados para confecção de estruturas monolíticas e reparos em alvenarias refratárias submetidas ao ataque químico por escórias básicas. Fornecidos em sacos multifolhados de papel ou em big bags. O concreto BASICAST-2873 emprega o ligante especial, o qual é enviado separadamente. |
Recommended for the manufacture of monolithic structures and brick repairs subjected to chemical attack by basics slags. Packaged in multi-ply paper bags or in big bags. BASICAST-2873 uses a special binder, sent separately. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
M |
Fe2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| BASICAST-2873 |
89,5 |
1,9 |
2,50 |
25 |
40 |
0,0 |
-1,2 |
| BASICAST |
76,0 |
2,0 |
2,30 |
10 |
15 |
0,0 |
1,5 |
| Recomendados para confecção de estruturas monolíticas que devam apresentar elevada resistência mecânica a quente e alta refratariedade. Fornecidos em sacos multifolhasdos de papel ou em big bags. Os concretos CFS empregam o ligante especial, o qual é enviado separadamente. |
Recommended for the manufacture of monolithic structures of high mechanical resistence at elevated temperatures and high refractoriness. Packaged in multi-ply paper bags or in big bags. CFS uses a special binder, sent separately. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
Fe2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CASTOGNI-CF-95 |
94,5 |
4,5 |
0,2 |
2,82 |
30 |
80 |
0,0 |
-0,5 |
| CASTOGNI-CF-95-W |
94,5 |
4,5 |
0,2 |
2,85 |
30 |
90 |
0,0 |
-0,5 |
| CASTOGNI-CF-90 |
90,0 |
8,4 |
0,8 |
2,80 |
20 |
70 |
0,0 |
-0,5 |
| CASTOGNI-CF-80 |
80,5 |
15,5 |
1,6 |
2,60 |
15 |
50 |
0,0 |
-0,5 |
| CASTOGNI-CF-MTW |
72,0 |
27,0 |
0,3 |
2,50 |
25 |
60 |
0,0 |
-0,2 |
| CASTOGNI-CF-70 |
70,0 |
26,0 |
1,5 |
2,40 |
25 |
60 |
0,0 |
-0,2 |
| CASTOGNI-CF-60 |
60,0 |
36,0 |
1,5 |
2,20 |
15 |
45 |
0,0 |
-1,0 |
| CASTOGNI-CF-50 |
50,0 |
46,0 |
1,8 |
2,10 |
14 |
40 |
0,0 |
-1,0 |
| CASTOGNI-CFS-95 W |
94,9 |
5,2 |
0,1 |
3,15 |
34 |
110 |
-0,1 |
-0,2 |
| CASTOGNI-CFS-95 |
94,5 |
4,9 |
0,2 |
2,85 |
35 |
80 |
0,0 |
-0,4 |
| CASTOGNI-CFS-90 |
90,1 |
7,0 |
0,7 |
3,12 |
14 |
121 |
0,0 |
-0,3 |
| CASTOGNI-CFS-80 |
80,2 |
14,7 |
1,3 |
2,79 |
18 |
104 |
0,0 |
0,8 |
| CASTOGNI-CFS-MTW |
72,0 |
27,0 |
0,3 |
2,53 |
26 |
55 |
-0,1 |
-0,2 |
| CASTOGNI-CFS-130 |
72,5 |
7,7 |
0,1 |
2,85 |
13 |
95 |
0,0 |
-0,1 |
| CASTOGNI-CFS-70 |
69,6 |
24,6 |
1,8 |
2,39 |
16 |
58 |
-0,1 |
-0,1 |
| CASTOGNI-CFS-60 |
59,6 |
34,1 |
2,4 |
2,25 |
11 |
58 |
-0,1 |
-0,8 |
| CASTOGNI-CFS-50 |
57,3 |
37,9 |
1,6 |
2,27 |
17 |
79 |
-0,1 |
-0,8 |
| Recomendado para confecção de estruturas monolíticas e peças especiais de alta complexidade, com fácil enchimento das fôrmas sem necessidade do uso de vibradores para adensamento. Fornecidos em sacos multifolhados de papel ou big bags. |
Recommended for the manufacture of monolithic structures and high complexity special pieces, with easy mould-filling that does not require vibrating for consolidation. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
CaO |
Cr2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CASTOGNI-SF-90 |
90,0 |
5,5 |
1,7 |
- |
2,95 |
60 |
90 |
0,0 |
-1,0 |
| CASTOGNI-SF-90-C |
89,0 |
3,5 |
1,4 |
4,0 |
3,00 |
45 |
67 |
0,0 |
-0,5 |
| CASTOGNI-SF-80 |
80,5 |
13,0 |
1,4 |
- |
2,75 |
65 |
65 |
0,0 |
-0,1 |
| CASTOGNI-SF-MTW |
72,0 |
25,5 |
1,7 |
- |
2,55 |
55 |
75 |
0,0 |
-0,6 |
| CASTOGNI-SF-70 |
71,0 |
22,0 |
1,8 |
- |
2,40 |
35 |
75 |
0,0 |
-0,6 |
| CASTOGNI-090-SP (*) |
64,5 |
12,8 |
2,3 |
17,5(SiC) |
2,69 |
30 |
25 |
0,0 |
1,5 |
| CASTOGNI-SF-50 |
50,0 |
45,4 |
1,7 |
- |
2,20 |
30 |
73 |
0,0 |
-0,6 |
| (*) Também aplicável por shotcrete / Also for shotcrete application |
| Recomendados para confecção de estruturas monolíticas de alta resistência mecânica, submetidas à intensa abrasão ou erosão em variadas temperaturas. Fornecidos em sacos multifolhados de papel ou em big bags. |
Recommended for the manufacture of monolithic structures of high mechanical resistence, subjected to intense abrasion or erosion at various temperatures. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
CaO |
Cr2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CASTOGNI-3022-LC |
95,0 |
0,7 |
2,5 |
- |
2,80 |
20 |
28 |
0,0 |
0,3 |
| CASTOGNI-90-WLC |
92,0 |
5,0 |
1,5 |
- |
3,00 |
65 |
60 |
0,0 |
0,0 |
| CASTOGNI-WS-LC |
91,2 |
0,8 |
1,7 |
- |
3,00 |
26 |
35 |
-0,1 |
0,7 |
| CASTOGNI-2375-LC (*) |
90,9 |
2,1 |
1,7 |
- |
3,00 |
50 |
50 |
0,0 |
0,2 |
| CASTOGNI-90-LC |
90,0 |
6,0 |
1,5 |
- |
3,00 |
60 |
50 |
0,0 |
0,0 |
| CASTOGNI-90-WLCC |
90,0 |
3,0 |
1,3 |
5,0 |
2,90 |
68 |
60 |
0,0 |
0,0 |
| CASTOGNI-90-LCC |
88,0 |
4,7 |
1,6 |
3,9 |
3,00 |
60 |
50 |
-0,1 |
-0,5 |
| CASTOGNI-85-LC |
85,0 |
11,1 |
2,1 |
- |
2,75 |
70 |
60 |
0,0 |
-1,0 |
| CASTOGNI-90-WLCC-M |
82,9 |
5,2 |
1,3 |
10,0 |
2,95 |
25 |
52 |
0,0 |
-0,2 |
| CASTOGNI-2970-LC |
82,6 |
10,7 |
2,0 |
- |
2,70 |
60 |
63 |
0,0 |
-1,0 |
| CASTOGNI-85-LCC |
81,5 |
10,3 |
2,0 |
3,0 |
2,87 |
85 |
75 |
0,0 |
-1,0 |
| CASTOGNI-80-LC |
80,0 |
14,0 |
2,1 |
- |
2,70 |
70 |
50 |
0,0 |
-1,0 |
| CASTOGNI-80-LCC |
80,0 |
12,2 |
2,0 |
3,0 |
2,70 |
60 |
50 |
0,0 |
-1,0 |
| CASTOGNI-2886/2 |
80,0 |
15,5(SiO2+SiC) |
2,3 |
- |
3,00 |
70 |
50 |
0,0 |
-0,3 |
| CASTOGNI-2086/4-LC |
77,0 |
14,6(SiO2+SiC) |
2,4 |
3,0 |
3,16 |
98 |
84 |
0,0 |
0,0 |
| CASTOGNI-MTW-LC-M |
72,3 |
25,2 |
1,5 |
- |
2,50 |
50 |
60 |
-0,2 |
-0,5 |
| CASTOGNI-MTW-LC |
72,0 |
24,0 |
1,6 |
- |
2,50 |
50 |
50 |
0,0 |
-0,6 |
| CASTOGNI-1750/3-LC |
71,0 |
22,0(SiO2+SiC) |
2,4 |
- |
2,65 |
55 |
50 |
0,0 |
-0,2 |
| CASTOGNI-MTW-LCC |
70,6 |
22,9 |
1,4 |
4,0 |
2,50 |
50 |
48 |
-0,1 |
-1,0 |
| CASTOGNI-70-LC |
70,5 |
21,7 |
2,4 |
- |
2,50 |
70 |
60 |
0,0 |
0,0 |
| CASTOGNI-3813 |
63,0 |
34,0(SiO2+SiC) |
1,6 |
- |
2,80 |
40 |
45 |
0,0 |
1,8 |
| CASTOGNI-60-LC |
60,5 |
34,5 |
2,4 |
- |
2,45 |
80 |
50 |
0,0 |
0,2 |
| CASTOGNI-60-LCC |
57,0 |
31,8 |
2,4 |
3,0 |
2,45 |
70 |
50 |
0,0 |
0,2 |
| CASTOGNI-50-LC |
53,5 |
40,1 |
2,3 |
- |
2,35 |
60 |
50 |
0,0 |
1,5 |
| CASTOGNI-50-MZ-LC |
53,5 |
18,5 |
1,5 |
25,8(ZrO2) |
2,95 |
48 |
50 |
0,0 |
-0,2 |
| CASTOGNI-125-LC |
51,6 |
41,7(SiO2+SiC) |
1,7 |
- |
2,30 |
58 |
54 |
0,1 |
-0,3 |
| CASTOGNI-45-LC |
45,5 |
47,5 |
2,4 |
- |
2,30 |
60 |
50 |
0,0 |
-1,0 |
| CASTOGNI-3805 |
38,7 |
56,0(SiO2+SiC) |
1,7 |
- |
2,34 |
32 |
60 |
-0,1 |
0,6 |
| CASTOGNI-3049-LC |
10,6 |
86,2 |
2,4 |
- |
1,85 |
40 |
17 |
0,0 |
2,7 |
| (*) Alumina-Espinélio |
| Recomendados para aplicação por projeção pneumática. Fornecidos em sacos multifolhados de papel ou em big bags. |
Recomended for application by gunning. Packaged in multi-ply paper bags or big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
CaO |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CASTOGNI-G-90 |
90,0 |
2,5 |
4,5 |
2,60 |
20 |
35 |
-0,1 |
-1,1 |
| CASTOGNI-G-80 HG (*) |
84,0 |
9,3 |
1,7 |
2,55 |
10 |
20 |
-0,1 |
-1,0 |
| CASTOGNI-G-80 |
80,0 |
10,0 |
6,2 |
2,45 |
15 |
35 |
-0,2 |
-1,0 |
| CASTOGNI-G-70 |
71,0 |
18,6 |
6,5 |
2,15 |
20 |
30 |
-0,4 |
-1,0 |
| HARD-GUN |
61,7 |
6,7 |
12,4 |
2,56 |
50 |
45 |
0,0 |
-0,6 |
| CASTOGNI-G-60 |
60,0 |
32,5 |
6,2 |
2,00 |
20 |
30 |
-0,4 |
-1,0 |
| CASTOGNI-G-50 |
50,0 |
39,0 |
6,2 |
2,00 |
20 |
40 |
-0,4 |
-1,0 |
| CASTOGNI-G-41 |
43,0 |
47,0 |
6,0 |
2,00 |
14 |
26(1200ºC) |
-0,4 |
-1,8(1200ºC) |
| (*) Projeção a quente |
| Recomendados para confecção de estruturas monolíticas e peças especiais. Fornecidos em sacos multifolhados de papel ou em big bags. |
Recommended for monolithic and special pieces. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
CaO |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CASTOGNI-90-S |
90,0 |
1,3 |
4,5 |
2,90 |
28 |
50 |
0,0 |
-1,0 |
| CASTOGNI-90 |
90,0 |
2,0 |
4,5 |
2,75 |
20 |
50 |
-0,1 |
-1,1 |
| CASTOGNI-85-S |
85,5 |
5,3 |
5,5 |
2,70 |
30 |
40 |
-0,1 |
0,2 |
| CASTOGNI-85 |
85,5 |
5,3 |
5,5 |
2,60 |
30 |
30 |
-0,2 |
-1,2 |
| CASTOGNI-85-F (*) |
84,5 |
7,0 |
5,0 |
2,55 |
30 |
40 |
-0,2 |
-1,5 |
| CASTOGNI-3392 |
81,4 |
9,3 |
5,9 |
2,35 |
20 |
25 |
-0,1 |
-1,5 |
| CASTOGNI-80-S |
80,0 |
10,0 |
5,3 |
2,70 |
35 |
35 |
0,0 |
-0,4 |
| CASTOGNI-80 |
80,0 |
11,0 |
5,5 |
2,55 |
35 |
35 |
0,3 |
-1,0 |
| CASTOGNI-70-F (*) |
71,0 |
19,0 |
5,0 |
2,20 |
20 |
45 |
-0,2 |
-1,6 |
| CASTOGNI-70 |
70,5 |
19,5 |
5,5 |
2,20 |
25 |
45 |
-0,4 |
-1,3 |
| CASTOGNI-70-S |
70,0 |
19,0 |
5,5 |
2,35 |
40 |
50 |
0,0 |
-0,8 |
| HARD CAST |
62,3 |
5,1 |
12,8 |
2,70 |
46 |
50 |
-0,2 |
-0,8 |
| CASTOGNI-60-F (*) |
62,0 |
27,0 |
5,9 |
2,30 |
25 |
40 |
-0,5 |
-1,0 |
| CASTOGNI-60 |
62,0 |
27,0 |
5,9 |
2,10 |
25 |
40 |
-0,5 |
-1,0 |
| CASTOGNI-60-S |
62,0 |
27,0 |
5,5 |
2,20 |
40 |
45 |
0,0 |
-0,4 |
| CASTOGNI-2118-D |
60,0 |
26,0 |
6,5 |
2,10 |
40 |
45 |
-0,2 |
-0,4 |
| CASTOGNI-51-E |
55,0 |
33,0 |
7,2 |
2,15 |
30 |
36 |
-0,4 |
-1,3 |
| CASTOGNI-50 |
54,0 |
34,0 |
6,7 |
2,10 |
30 |
40 |
-0,4 |
-1,0 |
| CASTOGNI-45 (*) |
42,0 |
48,7 |
6,0 |
2,10 |
20 |
40 |
0,0 |
-1,0 |
| CASTOGNI-42 |
42,0 |
48,7 |
6,0 |
2,10 |
25 |
35 |
-0,2 |
-0,3 |
| CASTOGNI-N |
41,5 |
50,0 |
3,7 |
2,05 |
20 |
30 |
-0,2 |
0,3 |
| (*) Estes produtos apresentam boa aderência quando aplicados com colher / These products present a od adhrence when applied with trowel. |
| Recomendados para revestimentos monolíticos onde se requer isolamento térmico. Fornecidos em sacos multifolhados ou em big bags. |
Recommended for monolithic linings where insulation is required. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Temperatura Máxima de Utilização
Maximum Recommended Service Temperature |
Condutividade Térmica (W/m.K)
Thermal Conductivity (W/m.K) |
| |
Al2O3 |
CaO |
Fe2O3 |
(g/cm³) |
(MPa) |
(ºC) |
500ºC | 800ºC | 1100ºC |
| LAITOGNI-2969/4 |
13,1 |
34,3 |
4,8 |
0,42 |
0,5 |
1 000 |
0,26 |
0,29 |
0,26 |
| LAITOGNI-2969/6 |
16,7 |
34,15 |
4,0 |
0,57 |
1,1 |
1 000 |
0,25 |
0,28 |
0,25 |
| LAITOGNI-LV |
11,0 |
42,0 |
3,4 |
0,80 |
2 |
800 |
0,26 |
0,29 |
- |
| LAITOGNI-PAV |
20,2 |
32,0 |
3,3 |
0,85 |
2 |
1 000 |
0,26 |
0,29 |
0,26(1000ºC) |
| LAITOGNI-AE10 |
13,5 |
34,5 |
4,4 |
1,00 |
5,5 |
1 000 |
0,26 |
0,29 |
0,26 |
| LAITOGNI-1211 |
35,5 |
12,5 |
2,0 |
1,00 |
10 |
1 200 |
0,26 |
0,29 |
0,37 |
| LAITOGNI-1010 |
20,0 |
34,0 |
2,8 |
1,00 |
5 |
1 000 |
0,26 |
0,29 |
0,34(1000ºC) |
| LAITOGNI-1011 |
49,0 |
17,0 |
2,0 |
1,10 |
5 |
1 000 |
0,31 |
0,35 |
0,41(1000ºC) |
| LAITOGNI-AE11 |
41,3 |
16,6 |
3,9 |
1,10 |
5,6 |
1 000 |
0,31 |
0,35 |
0,43 |
| LAITOGNI-95 |
94,0 |
4,7 |
0,1 |
1,25 |
7 |
1 800 |
0,80 |
0,73 |
0,76 |
| LAITOGNI-1113 |
23,0 |
34,0 |
2,0 |
1,30 |
7 |
1 100 |
0,44 |
0,50 |
0,58 |
| LAITOGNI-40 |
42,5 |
12,3 |
2,0 |
1,40 |
6 |
1 300 |
0,52 |
0,57 |
0,67 |
| LAITOGNI-L |
29,0 |
25,5 |
1,5 |
1,50 |
12 |
1 200 |
0,57 |
0,64 |
0,71 |
| LAITOGNI-LE |
52,0 |
9,0 |
1,0 |
1,60 |
12 |
1 450 |
0,64 |
0,67 |
0,76 |
| Recomendados para confecção de estruturas monolíticas e reparos em alvenarias refratárias. Os plásticos de liga fosfática desenvolvem alta resistência em temperaturas baixas. São fornecidos na forma plástica ou moldável prontos para o uso, embalados em caixas de papelão. |
Recommended for the manufacture of monolithic structures and for refractory brick repairs. Phosphate-bounded plastics develop high resistence at low temperatures. Supplied in plastic form or for molding, ready for use, packaged in cartogniard boxes. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
Cr2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CERPLAST-90-LF |
93,5 |
- |
2,75 |
25 |
30 |
0,0 |
-1,0 |
| CERPLAST-90-CRLF |
90,0 |
4,0 |
2,95 |
28 |
45 |
0,2 |
-0,5 |
| CERPLAST-80-LF |
82,5 |
- |
2,55 |
15 |
20 |
-0,1 |
0,2 |
| CERPLAST-80-CRLF |
82,0 |
4,0 |
2,60 |
16 |
25 |
0,0 |
0,8 |
| Recomendados para confecção de estruturas monolíticas e reparos em alvenarias refratárias. São fornecidos na forma plástica ou moldável prontos para uso, embalados em caixas de papelão. |
Recommended for the manufacture of monolithic structures and for repair work. Supplied in plastic form or for molding, ready for use, packaged in cartogniard boxes. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| CERPLAST-81 |
81,5 |
15,0 |
2,60 |
10 |
20 |
0,2 |
0,8 |
| CERPLAST-80 |
80,3 |
16,2 |
2,55 |
12 |
16 |
-0,4 |
1,0 |
| CERPLAST-70 |
70,0 |
26,0 |
2,50 |
13 |
18 |
-0,4 |
0,4 |
| CERPLAST-60 |
61,5 |
34,0 |
2,20 |
10 |
12 |
-0,4 |
0,0 |
| CERPLAST-50 |
52,0 |
44,0 |
2,15 |
8 |
12 |
-0,6 |
-0,5 |
| CERPLAST-40 |
50,0 |
46,0 |
2,15 |
8 |
12 |
-0,6 |
-0,5 |
| CERPLAST-CQZ |
11,5 |
86,5 |
2,00 |
3 |
4 |
0,5 |
0,0 |
| CERPLAST-QS |
10,2 |
88,0 |
2,00 |
4 |
5 |
-0,5 |
0,0 |
| Recomendadas para o revestimento de soleiras e rampas de Fornos Elétricos a Arco dos processos metalúrgicos básicos. Fornecidas em sacos multifolhados de papel ou em big bags. |
Recommended for use in hearths and ramps of Eletric Arc Furnaces in basic metallurgical processes. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
M |
Fe2O3 |
(g/cm³) |
(MPa) |
(%) |
| RAM-TOG 2163/1 |
80,5 |
7,0 |
2,90 |
40 |
-1,5 |
| RAM-TOG 2163/2 |
80,5 |
7,0 |
2,90 |
60 |
-1,0 |
| Recomendadas para confecção de estruturas monolíticas, peças especiais e reparos em alvenarias de fornos. As massas de socar de pega fosfática desenvolvem alta resistência em temperaturas baixas. Fornecidas em sacos multifolhados de papel e o ligante fosfórico é enviado separadamente. |
Recommended for the manufacture of monolithic structures, special pieces and for furnace lining repair work. Phosphate-bonded ramming mixes develop high resistence at low temperatures. Packaged in multi-ply paper bags; the phosphoric binder is sent separately. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
Fe2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| MARTEL-90-LF |
90,0 |
1,0 |
2,80 |
25 |
40 |
0,0 |
-0,8 |
| MARTEL-80-LF |
80,0 |
1,2 |
2,50 |
15 |
30 |
0,0 |
-0,8 |
| MARTEL-70-LF |
71,0 |
2,0 |
2,30 |
20 |
35 |
-0,1 |
-1,2 |
| MARTEL-60-LF |
60,0 |
2,2 |
2,20 |
20 |
20 |
-0,2 |
-1,2 |
| Recomendadas para confecção de estruturas monolíticas, peças especiais e reparos em alvenarias de fornos. São fornecidas em baldes já com a umidade correta para utilização. |
Recommended for the manufacture of monolithic structures, special pieces and for furnace lining repair work. Supplied in pails with correct humidity for use. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Densidade Aparente
Bulk Density |
Resistência à Compressão após 110ºC
Cold Crushing Strength after Drying at 110ºC |
Resistência à Compressão após 1450ºC
Cold Crushing Strength after Heating at 1450ºC |
Variação Linear Dimensional após 110ºC
Permanent Linear Change after Drying at 110ºC |
Variação Linear Dimensional após 1450ºC
Permanent Linear Change after Heating at 1450ºC |
| |
Al2O3 |
Fe2O3 |
(g/cm³) |
(MPa) |
(MPa) |
(%) |
(%) |
| REPAR-95 |
92,0 |
1,0 |
3,00 |
40 |
60 |
0,0 |
-0,4 |
| REPAR-70 |
70,5 |
1,4 |
2,30 |
9 |
20 |
0,0 |
-0,3 |
| REPAR-2322 |
68,3 |
1,0 |
2,60 |
6 |
40 |
0,0 |
0,0 |
| REPAR-60 |
60,0 |
2,1 |
2,15 |
7 |
12 |
0,0 |
-0,3 |
| REPAR-50 |
54,0 |
2,2 |
2,05 |
10 |
12 |
0,0 |
-0,4 |
| Recomendadas para o assentamento de peças refratárias básicas. Desenvolvem pega a temperatura ambiente e seu preparo requer adição de água. Fornecidas em sacos multifolhados de papel. |
Recommended for the laying of basic refractory pieces. Setting is developed at room temperature and preparation requires water addition. Packaged in multi-ply paper bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Força Ligante após 110ºC
Bonding Strength after Drying at 110ºC |
Força Ligante após 1450ºC
Bonding Strength after Heating at 1450ºC |
Água de Amassamento
Added Water |
| |
MgO |
Cr2O3 |
Fe2O3 |
(MPa) |
(MPa) |
(litros/100kg) |
| BASIFIX |
75,5 |
5,5 |
2,2 |
3 |
2 |
20-26 |
| BASIFIX-MCS |
51,8 |
15,3 |
6,4 |
2 |
2,5 |
20-26 |
| Recomendadas para o assentamento de peças refratárias. Desenvolvem pega a temperatura ambiente e seu preparo requer adição de água. Fornecidas em sacos multifolhados de papel. |
Recommended for the laying of refractory pieces. Setting is developed at room temperature and preparation requires water addition. Packaged in multi-ply paper bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Força Ligante após 110ºC
Bonding Strength after Drying at 110ºC |
Força Ligante após 1450ºC
Bonding Strength after Heating at 1450ºC |
Água de Amassamento
Added Water |
| |
Al2O3 |
SiO2 |
Fe2O3 |
SiC |
C |
(MPa) |
(MPa) |
(litros/100kg) |
| FIX-AR-90 |
90,5 |
6,5 |
0,8 |
- |
- |
3 |
3 |
12-15 |
| FIX-AR-86 |
86,5 |
10,0 |
1,3 |
- |
- |
2 |
3 |
17-21 |
| FIX-AR-80 |
80,0 |
17,2 |
1,6 |
- |
- |
3 |
3 |
16-21 |
| FIX-AR-2460 |
72,0 |
4,5 |
0,7 |
15,5 |
5,0 |
3 |
4 |
20-23 |
| FIX-AR-70 |
70,0 |
22,5 |
1,4 |
- |
- |
3 |
2 |
22-26 |
| FIX-AR-MZ |
61,3 |
23,9 |
0,4 |
- |
- |
2 |
3 |
14-17 |
| FIX-AR-60 |
60,0 |
35,0 |
2,0 |
- |
- |
3 |
3 |
18-22 |
| FIX-AR-50 |
54,5 |
39,0 |
2,9 |
- |
- |
2 |
3 |
21-25 |
| FIX-AR-42 |
45,5 |
48,0 |
2,5 |
- |
- |
2 |
4 |
20-24 |
| Recomendadas para o assentamento de peças refratárias em locais sujeitos ao ataque por álcalis. Desenvolvem pega a baixa temperatura e seu preparo requer adição do ligante fosfórico enviado separadamente. Fornecidas em sacos multifolhados de papel. |
Recommended for the laying of refratory pieces in places that are subject to alkali attack. Setting is developed at low temperature and preparation requires the use of a phophoric binder, sent separately. Packaged in multi-ply paper bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Força Ligante após 110ºC
Bonding Strength after Drying at 110ºC |
Força Ligante após 1450ºC
Bonding Strength after Heating at 1450ºC |
Ligante de Amassamento
Binder |
| |
Al2O3 |
SiO2 |
Cr2O3 |
Fe2O3 |
(MPa) |
(MPa) |
(litros/100kg) |
| ALSET-W-90 |
90,0 |
9,0 |
- |
0,6 |
7 |
9 |
32 |
| ALSET-86 |
86,0 |
10,0 |
- |
0,8 |
6 |
7 |
38 |
| ALCRO-90 |
85,0 |
7,0 |
4,5 |
1,0 |
8 |
10 |
32 |
| ALSET-70 |
70,0 |
25,5 |
- |
1,6 |
6 |
8 |
33 |
| ALSET-60 |
60,0 |
34,5 |
- |
1,8 |
7 |
12 |
32 |
| ALSET-50 |
52,0 |
43,0 |
- |
2,3 |
4 |
10 |
36 |
| Recomendadas para o assentamento de peças refratárias. A pega definitiva é obtida a alta temperatura e seu preparo requer adição de água. Fornecidas em sacos multifolhados de papel. |
Recommended for the laying of refractory pieces. Definitive setting is obtained at high temperature and preparation requires water addition. Packaged in multi-ply paper bags or in big bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Água de Amassamento
Added Water |
| |
Al2O3 |
SiO2 |
Fe2O3 |
(litros/100kg) |
| T-72 |
72,0 |
23,0 |
2,5 |
30-35 |
| T-62 |
60,0 |
34,0 |
2,3 |
30-35 |
| CT-2 |
55,0 |
38,5 |
2,5 |
35-40 |
| T-51 |
53,0 |
42,0 |
2,5 |
35-40 |
| ISOTOGNI-40 |
43,5 |
48,5 |
2,3 |
48-52 |
| FIX-AR-2409 (*) |
9,2 |
85,6 |
0,5 |
- |
| (*) Aplicação a seco / Dry application |
| Recomedadas para o assentamento de peças antiácidas. Desenvolvem pega a temperatura ambiente e seu preparo requer adição do ligante especial enviado separadamente. Fornecidas em sacos multifolhados de papel. |
Recommended for the laying of anti-acid pieces. Setting is developed at room temperature and preparation requires the use of a special binder, sent separately. Packaged in multi-ply paper bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Força Ligante após 110ºC
Bonding Strength after Drying at 110ºC |
Ligante de Amassamento
Binder |
| |
Al2O3 |
SiO2 |
Fe2O3 |
(MPa) |
(litros/100kg) |
| CTRA |
3,0 |
91,0 |
0,6 |
3 |
40-45 |
| TSRA |
3,0 |
91,0 |
0,6 |
2 |
57-61 |
| Recomendada para pintura de proteção ou acabamento em vários revestimentos refratários. O seu preparo requer adição de água. Fornecida em sacos multifolhados de papel. |
Recommended for protective painting or for coating finish on various refractory linings. Preparation requires water addition. Packaged in multi-ply paper bags. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Água de Amassamento
Added Water |
| |
Al2O3 |
SiO2 |
Fe2O3 |
(litros/100kg) |
| PLAST-PAINT |
88,0 |
9,0 |
1,5 |
26-30 |
| Recomendadas para assentamento de peças refratárias. Desenvolvem pega a temperatura ambiente. Fornecidas em baldes, prontas para uso. |
Recommended for the laying of refractory pieces. Setting is developed at room temperatura. Supplied in pails, ready for use. |
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Força Ligante após 110ºC
Bonding Strength after Drying at 110ºC |
Força Ligante após 1450ºC
Bonding Strength after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
Fe2O3 |
(MPa) |
(MPa) |
| FIX-AR-91 |
90,5 |
7,0 |
0,3 |
3 |
3 |
| FIX-AR-81 |
80,0 |
16,0 |
1,5 |
3 |
3 |
| FIX-AR-71 |
70,0 |
25,0 |
1,9 |
3 |
4 |
| FIX-AR-3484 |
60,4 |
34,6 |
1,8 |
9 |
12 |
| FIX-AR-61 |
60,0 |
35,0 |
2,3 |
2 |
4 |
| FIX-AR-51 |
56,0 |
38,0 |
2,3 |
2 |
4 |
| FIX-AR-3219 |
53,6 |
38,8 |
2,2 |
6 |
15 |
| FIX-AR-41 |
46,0 |
49,0 |
2,3 |
2 |
4 |
|
|
MARCA
Brand |
Análise Química
Chemical Analysis
(%) |
Força Ligante após 110ºC
Bonding Strength after Drying at 110ºC |
Força Ligante após 1450ºC
Bonding Strength after Heating at 1450ºC |
| |
Al2O3 |
SiO2 |
Fe2O3 |
(MPa) |
(MPa) |
| FIX-AR-C1-3 |
54,5 |
40,0 |
2,3 |
8 |
9 |
|
|
|
| |
|
|
|